ong glass fiber reinforced Nylon 6 (PA6 LGF50) is a special type of polyamide designed for tough and heavy-duty use. It has 50% long glass fibers, which makes it incredibly strong and resistant to wear and tear. This engineered nylon is perfect for making car parts that need to be durable and lightweight.
Long glass fiber reinforced Nylon 6 (PA6 LGF50) is a special type of polyamide designed for tough and heavy-duty use. It has 50% long glass fibers, which makes it incredibly strong and resistant to wear and tear. This engineered nylon is perfect for making car parts that need to be durable and lightweight.
PA6 LGF50 has excellent mechanical strength, which allows it to replace metal in many automotive applications. Its lightweight nature helps reduce vehicle weight, improving fuel efficiency. Plus, its ability to resist heat and maintain its shape under stress makes it ideal for parts like engine mounts, brackets, and other structural components in cars.
The addition of long glass fibers to PA6 makes this material even more robust than regular polyamide. These fibers run through the material, giving it extra strength and stiffness. This reinforcement helps the material withstand impact, making it perfect for automotive parts that face constant pressure and heat. It’s also resistant to moisture and chemicals, so it lasts longer in tough environments.
Mechanical strength | parameter | value | unit | norm |
Tensile strength | 50mm/min | 195 | Mpa | ISO 527-2 |
Elongation at Break | 50mm/min | 3.0 | % | ISO 527-2 |
Flexural Strength | 2mm/min | 300 | Mpa | ISO 178 |
Flexural Modulus | 2mm/min | 12000 | Mpa | ISO 178 |
Izod Notched Impact Strength | 23℃ | 14 | kJ/m2 | ISO 180 |
Thermal performance | parameter | value | unit | norm |
Temperature of Deflection Under Load | 1.8MPa | 210 | ℃ | ISO 75 |
Temperature of Deflection Under Load | 0.45MPa | 218 | ℃ | ISO 75 |
Melting temperature | / | 220 | ℃ | ISO 11375 |
Electrical properties | parameter | value | unit | norm |
Surface resistivity | / | 1014 | Ω | / |
Volume resistivity | / | 1015 | Ω | / |
Other properties | parameter | value | unit | norm |
Water absorption | 23℃,24h | 0.7 | % | ISO 62 |
Flammability | / | HB | class | UL94 |
Glass fiber filler | 1h（600） | 50 | % | ISO 3451 |
This 50% long GF reinforced PA6 achieves 200MPa tensile strength (ISO 527-2), 20kJ/m² impact (ISO 179-1), and 220℃ HDT at 1.82MPa (ISO 75-1), reducing weight by 40% vs aluminum. Validated for >1×10^6 fatigue cycles (ASTM D638) and oil resistance (ASTM D471). Fiber orientation optimized via ISO 10724, 0.6% shrinkage (ISO 294-4) ensures sealing precision. Thermal conductivity 0.8W/m·K (ASTM E1461) supports heat dissipation.
Polyamide 6 Long Glass Fiber Reinforced With 50% Glass Fiber For Plumbing Valve Cores
With 190MPa tensile strength (ASTM D638) and 18kJ/m² impact (ASTM D256), this material withstands 180℃ continuous temperature (ISO 75-2). Validated for 6.5MPa burst pressure (ISO 1167) and chemical resistance (ASTM D543). 35% lighter than brass, 30% shorter cycle time via ISO 1133 MVR data. Bending modulus 12GPa (ISO 178), HRR 110 hardness (ASTM D785) resists wear, compatible with ISO 1501 thread molding.
Frequently asked questions about Engineered Polyamide Compound manufacturing
Our preferred payment methods are T/T. However, we are open to discussing L/C, Paypal upon request.
Yes, we conduct 100% testing on all goods prior to delivery.
We are a polyamide factory.
Engineered polyamide compounds are used in various industries such as automotive parts, electrical components, consumer goods, and industrial machinery. They are commonly found in gears, bearings, electrical housings, and under-the-hood automotive components due to their durability and resistance to heat and chemicals.
Standard delivery time is 7-14 days if the item is in stock. If not, it may take 15-20 days to arrange shipment.
Yes, we can match material colors based on your specified Pantone or RAL number.
© Copyright 2024 Modified Nylon. All right reserved.