UV-resistant PA6 GF30 is a high-performance material designed for outdoor use. It’s made from polyamide 6 (also known as nylon) and is reinforced with 30% glass fibers. This combination makes the material strong, durable, and able to withstand harsh sunlight. It is especially useful for products that need extra toughness in extreme weather conditions.
The 30% glass fiber content in this polyamide makes it significantly stronger and stiffer than standard nylon. This engineered nylon resists high temperatures and mechanical wear. It also has excellent resistance to impacts, making it perfect for outdoor parts like car components, industrial machinery, and electrical casings. Plus, its UV-resistant properties keep it from fading or breaking down over time, even when exposed to sunlight.
You’ll often see this polyamide 6 in industries where durability and strength are key. Some common uses include:
Its tough, long-lasting nature makes it a top choice for these heavy-duty uses.
Not only is this polyamide 6 engineered to resist UV rays, but it also fights against heat, cold, and even chemicals. When you need a material that won’t fail in harsh conditions, PA6 GF30 is an ideal choice. The glass fiber reinforcement ensures your product stays rigid and reliable, even after years of use outside.
Mechanical strength | parameter | value | unit | norm |
Tensile strength | 50mm/min | 160 | Mpa | ISO 527-2 |
Elongation at Break | 50mm/min | 3.5 | % | ISO 527-2 |
Flexural Strength | 2mm/min | 250 | Mpa | ISO 178 |
Flexural Modulus | 2mm/min | 8000 | Mpa | ISO 178 |
Izod Notched Impact Strength | 23℃ | 12 | kJ/m2 | ISO 180 |
Thermal performance | parameter | value | unit | norm |
Temperature of Deflection Under Load | 1.8MPa | 200 | ℃ | ISO 75 |
Temperature of Deflection Under Load | 0.45MPa | 210 | ℃ | ISO 75 |
Melting temperature | / | 220 | ℃ | ISO 11375 |
典型加工条件 Typical processing conditions | ||
注塑条件/Injection molding condition | 单位 | 典型值 |
干燥温度/Drying temperature | ℃ | 80~120 |
干燥时间/Drying time | h | 2~6 |
熔融温度/Melting temperature | ℃ | 230~270 |
注塑温度-喷嘴/Injection temperature – Nozzle | ℃ | 245~270 |
注塑温度-前段/Injection molding temperature – front section | ℃ | 230~245 |
注塑温度-中段/Injection molding temperature – middle section | ℃ | 240~250 |
注塑温度-后段/Injection molding temperature – post segment | ℃ | 250~270 |
模具温度/ Mold temperature | ℃ | 80~120 |
Electrical properties | parameter | value | unit | norm |
Surface resistivity | / | 1015 | Ω | / |
Volume resistivity | / | 1014 | Ω·cm | / |
Other properties | parameter | value | unit | norm |
Water absorption | 23℃，24h | 1.0 | % | ISO 62 |
Flammability | / | HB | class | UL94 |
Glass fiber filler | 1h（600℃） | 30 | % | ISO 3451 |
Nylon UV Resistance PA6 GF30 for Ice Skate Outsoles offers tensile strength ≥85 MPa (ISO 527-2:2023), notched impact strength 15 kJ/m² (ASTM D256-24), and HDT 160°C (0.45 MPa load). Glass-fiber reinforced polymer achieves 30% weight reduction with surface hardness Rockwell R110 (ISO 2039-2:2022). UV resistance (QUV 1000h) retains ≥95% tensile strength (ASTM D4329-23), while friction coefficient 0.25 (ASTM D1894-23) enhances glide performance.
Nylon UV Resistance PA6 GF30 for Plumbing System Components provides tensile strength ≥85 MPa (ISO 527-2:2023) and notched impact strength 18 kJ/m² (ASTM D256-24). Glass-fiber reinforced polymer achieves 35% weight reduction for plastic pipe connectors, with hydrostatic pressure resistance ≥2.8 MPa (ISO 1167-1:2023). Chlorine resistance (500h immersion, ASTM D543-22) shows ≤1.5% volume change, suitable for residential plumbing systems. Anti-biofilm properties meet ISO 846:2022.
Nylon UV Resistance PA6 GF30 for Automotive Fuel System Components provides tensile strength ≥90 MPa (ASTM D638-22) and unnotched impact strength >22 kJ/m² (ISO 179-1:2023). HDT 175°C (1.8 MPa) and fuel resistance (93# gasoline immersion, 500h) with ≤3% swelling (ASTM D471-22). Glass-fiber reinforced polymer achieves 40% weight reduction, maintaining ≥88% strength after 85°C/85% RH aging.
Frequently asked questions about Engineered Polyamide Compound manufacturing
Our preferred payment methods are T/T. However, we are open to discussing L/C, Paypal upon request.
Yes, we conduct 100% testing on all goods prior to delivery.
We are a polyamide factory.
Engineered polyamide compounds are used in various industries such as automotive parts, electrical components, consumer goods, and industrial machinery. They are commonly found in gears, bearings, electrical housings, and under-the-hood automotive components due to their durability and resistance to heat and chemicals.
Standard delivery time is 7-14 days if the item is in stock. If not, it may take 15-20 days to arrange shipment.
Yes, we can match material colors based on your specified Pantone or RAL number.