PA66 GF30’s ability to perform under elevated temperatures makes it highly favorable for applications like oven components, where heat resistance is crucial for product longevity.
PA66 GF30’s ability to perform under elevated temperatures makes it highly favorable for applications like oven components, where heat resistance is crucial for product longevity.
The Anti-Static Nylon Conductive Polyamide 66 Resin Granules (Virgin PA66 CF) is designed to offer excellent conductivity along with high tensile strength. With its anti-static properties, this engineered nylon ensures safety in environments where static electricity is a concern, such as electronics and sensitive equipment manufacturing.
Widely used across industries, including automotive, electronics, and mechanical engineering, this polyamide variant ensures high performance. Whether in automotive parts or electrical housings, its durability and anti-static features make it essential for advanced manufacturing.
The granules are available in various grades to suit different production needs. Fast delivery, free samples, and customization options make it easier for businesses to integrate this engineered nylon into their manufacturing processes.
Mechanical strength | parameter | value | unit | norm |
Tensile strength | 50mm/min | 130 | Mpa | ISO 527-2 |
Elongation at Break | 50mm/min | 5 | % | ISO 527-2 |
Flexural Strength | 2mm/min | 150 | Mpa | ISO 178 |
Flexural Modulus | 2mm/min | 8000 | Mpa | ISO 178 |
Izod Notched Impact Strength | 23℃ | 22 | kJ/m2 | ISO 179 |
Thermal performance | parameter | value | unit | norm |
Temperature of Deflection Under Load | 1.8MPa | 175 | ℃ | ISO 75 |
Temperature of Deflection Under Load | 0.45MPa | 180 | ℃ | ISO 75 |
Melting temperature | / | 190 | ℃ | ISO 11375 |
典型加工条件 Typical processing conditions | ||
注塑条件/Injection molding condition | 单位 | 典型值 |
干燥温度/Drying temperature | ℃ | 80~120 |
干燥时间/Drying time | h | 2~6 |
熔融温度/Melting temperature | ℃ | 270~300 |
注塑温度-喷嘴/Injection temperature – Nozzle | ℃ | 280~300 |
注塑温度-前段/Injection molding temperature – front section | ℃ | 270~280 |
注塑温度-中段/Injection molding temperature – middle section | ℃ | 275~290 |
注塑温度-后段/Injection molding temperature – post segment | ℃ | 280~300 |
模具温度/ Mold temperature | ℃ | 80~120 |
Electrical properties | parameter | value | unit | norm |
Surface resistivity | / | / | Ω | / |
Volume resistivity | / | / | Ω·cm | / |
Other properties | parameter | value | unit | norm |
Water absorption | 24h（23℃） | 0.15 | % | ISO 62 |
Flammability | / | HB | class | UL94 |
Glass fiber filler | 1h（600℃） | 30 | % | ISO 3451 |
Anti-Static Conductive PA66 CF for Anti-Static Tweezers delivers tensile strength ≥130 MPa (ASTM D638-22), notched impact strength 18 kJ/m² (ISO 180:2023), and heat deflection temperature 215°C (1.8 MPa load). Carbon fiber reinforcement reduces density to 1.32 g/cm³, achieving 30% weight reduction versus stainless steel. Surface resistivity (10^6-10^9Ω) meets ISO 61340-5-1:2021 for static control in semiconductor handling. Glass-fiber reinforced polymer technology ensures dimensional stability and durability in precision assembly.
Frequently asked questions about Engineered Polyamide Compound manufacturing
Our preferred payment methods are T/T. However, we are open to discussing L/C, Paypal upon request.
Yes, we conduct 100% testing on all goods prior to delivery.
We are a polyamide factory.
Engineered polyamide compounds are used in various industries such as automotive parts, electrical components, consumer goods, and industrial machinery. They are commonly found in gears, bearings, electrical housings, and under-the-hood automotive components due to their durability and resistance to heat and chemicals.
Standard delivery time is 7-14 days if the item is in stock. If not, it may take 15-20 days to arrange shipment.
Yes, we can match material colors based on your specified Pantone or RAL number.
© Copyright 2024 Modified Nylon. All right reserved.